Low coupling oxide media (lcom)

ABSTRACT

A low-coupling perpendicular magnetic recording media comprising a magnetic storage layer and at least one low saturation magnetization layer. The magnetic storage layer has a saturation magnetization between about 400-900 emu/cm 3  and the at least one low saturation magnetization layer has a saturation magnetization below that of the magnetic storage layer.

RELATED APPLICATION

None.

BACKGROUND

Magnetic discs with magnetizable media are used for data storage in most computer systems. According to the domain theory, a magnetic material is composed of a number of submicroscopic regions called domains. Each domain contains parallel atomic moments and is magnetized to saturation, but the directions of magnetization of different domains are not necessarily parallel. In the absence of an applied magnetic field, adjacent domains may be oriented randomly in any number of several directions, called the directions of easy magnetization, which depend on the geometry of the crystal. The resultant effect of all these various directions of magnetization may be zero, as is the case with an unmagnetized specimen. When a magnetic field is applied, the domains most nearly parallel to the direction of the applied field grow in size at the expense of the others. This is called boundary displacement of the domains or domain growth. A further increase in magnetic field causes more domains to rotate and align parallel to the applied field. When the material reaches the point of saturation magnetization, no further domain growth would take place on increasing the strength of the magnetic field.

The ease of magnetization or demagnetization of a magnetic material depends on the crystal structure, grain orientation, the state of strain, and the direction and strength of the magnetic field. The magnetization is most easily obtained along an easy axis of magnetization and most difficult along the hard axis of magnetization. A magnetic material is said to possess a magnetic anisotropy when easy and hard axes exist. On the other hand, a magnetic material is said to be isotropic when there are no easy or hard axes.

Many prior art magnetic recording media were fabricated with a longitudinal configuration. That is, the recording media were fabricated with in-plane (longitudinal) anisotropy in the magnetic layer. Longitudinal anisotropy results in magnetization forming in a direction in a plane parallel to the surface of the magnetic layer.

The demand for higher capacity magnetic recording media, however, has resulted in interest in perpendicular recording media; that is, recording media with a perpendicular anisotropy in the magnetic layer resulting in magnetization forming in a direction perpendicular to the surface of the magnetic layer. Typically, perpendicular recording media are fabricated with a polycrystalline CoCr alloy or CoPt-oxide alloy film. Co-rich areas in the polycrystalline film are ferromagnetic while Cr or oxide rich areas in the film are non-magnetic. Magnetic interaction between adjacent ferromagnetic domains are attenuated by the non-magnetic areas in between.

SUMMARY OF THE INVENTION

One embodiment of this invention relates to a low-coupling perpendicular magnetic recording media comprising a magnetic storage layer and at least one low saturation magnetization layer, wherein the magnetic storage layer has a saturation magnetization between about 400-900 emu/cm³ and the at least one low saturation magnetization layer has a saturation magnetization below that of the magnetic storage layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be better understood by reference to the Detailed Description of the Invention when taken together with the attached drawings, wherein:

FIG. 1 shows a magnetic recording medium according to one embodiment of the invention.

FIG. 2 shows a magnetic recording medium according to another embodiment of the invention.

FIG. 3 shows a magnetic recording medium according to a third embodiment of the invention.

FIG. 4 shows a magnetic recording medium according to a fourth embodiment of the invention.

FIG. 5 illustrates Monte Carlo simulations demonstrating improved recording properties of an embodiment of the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

As used in the specification and claims, the singular forms “a”, “an” and “the” include plural references unless the context clearly dictates otherwise.

The inventors have discovered that a weak uniform direct exchange coupling between magnetic grains in perpendicular recording media provides improved performance. The inventors have further discovered that weak uniform direct exchange coupling between the magnetic grains may be produced by adding a low saturation magnetization magnetic layer(s) in the perpendicular media structure. The inventors have additionally discovered that the strength of the direct exchange coupling can be controlled by varying saturation magnetization (Ms) of the magnetic layer.

An embodiment of this invention relates to a low-coupling perpendicular magnetic recording media comprising at least one low saturation magnetization layer, wherein the at least one low saturation magnetization layer has a saturation magnetization below 600 emu/cm³.

Another embodiment of the invention relates to a method of making a low-coupling perpendicular magnetic recording media comprising depositing an adhesion layer on a substrate, depositing a soft underlayer, depositing an non-magnetic interlayer, depositing a storage layer; and depositing a low saturation magnetization magnetic layer, wherein the at least one low saturation magnetization layer has a saturation magnetization below 600 emu/cm³.

Another embodiment of the invention relates to a method comprising obtaining a storage media having at least one layer with a saturation magnetization below 600 emu/cm³.

Additional advantages of this invention will become readily apparent to those skilled in this art from the following detailed description, wherein only a selection of preferred embodiments of this invention are shown and described, to illustrate the best modes contemplated for carrying out this invention. As will be realized, this invention may comprise other and different embodiments, and its details are capable of modifications in various obvious respects, all without departing from this invention. Accordingly, the drawings and description are to be regarded as illustrative in nature and not as restrictive.

EXAMPLES

All samples described in this disclosure were fabricated with DC magnetron sputtering except carbon films. Example data demonstrating the reduction of exchange coupling by reactive sputtering are explained herein.

FIG. 1 illustrates a first preferred embodiment of the invention. The low-coupling perpendicular magnetic recording media 10 of this embodiment includes a substrate 11, an adhesion layer 12, a soft under layer 13, an amorphous layer 14, a non-magnetic interlayer 15, a low-coupling magnetic layer 16, a storage layer 17, and a carbon protective overcoat. Optionally, the soft under layer 13, the amorphous layer 14, the non-magnetic interlayer 15, the low-coupling magnetic layer 16, the storage layer 17, and the carbon protective overcoat 18 may comprise multiple layers.

Preferred materials for the optional adhesion layer 12 include alloys containing one or more of Cr, Ni, Ta, and Ti. The choice depends on the substrate 11 and the material selected for the soft underlayer 13 and is within the skill of one of ordinary skill in the art. Preferably, the thickness of the adhesion layer is about 1-400 nm. More preferably, the thickness is about 2-20 nm.

Preferred materials for the soft underlayer 13 include alloys of at least one of Fe and Co with one or more elements selected from Ni, B, P, Si, C, Zr, Nb, Hf, Ta, Al, Si, Cu, Ag, Au. Preferably, the thickness of the soft underlayer 13 is about 10-400 nm. More preferably, the thickness is about 20-100 nm.

The amorphous layer 14 is optional. Preferred materials for the amorphous layer 14 include elements and alloys comprising Ta, Ti, Ni, Cr, Zr, Nb, and P, in compositions for which these alloys are amorphous. Other preferred materials include amorphous ferromagnetic materials consisting of Fe with one or more elements selected from Co, B, P, Si, C, Zr, Nb, Hf, Ta, Al, Si, Cu, Ag, and Au. Still other preferred materials include Ti_(x)Cr_(100-x) and Ta_(x)Cr_(100-x), where (30<x<60). Preferably, the thickness of the amorphous layer 14 is about 0-10 nm. More preferably the thickness is about 0.2-4 nm.

The crystallographic structure of the non-magnetic interlayer 15 depends on the crystallographic structure of the storage layer 17. For example, if the storage layer 17 is made of a Co-rich alloy with a hexagonal closed packed (hcp) structure, the non-magnetic interlayer 15 may include a face-centered cubic (fcc) layer of Cu, Ag, Au, Ir, Ni, Pt, Pd, or their alloys. Preferably, the thickness of this non-magnetic interlayer 15 ranges from about 0.2 nm to about 40 nm. More preferably, the thickness is about 1-20 nm. Alternatively, the non-magnetic interlayer 15 may include a hexagonal closed packed (hcp) layer of Ru, Re, Hf, Ti, Zr, or their alloys. Other hcp layers that may be used include Co and CoCr alloys. Optional additives to CoCr include Ta, B, Pt, Nb, Ru, Zr, and oxide materials. To use CoCr, the concentration of Cr and other alloying elements is chosen so that the alloy is non-magnetic and has an hcp crystal structure. To use Co-containing alloys the concentration of Cr and other alloying elements is chosen so that the alloy is non-magnetic and has an hcp crystal structure. Preferably, the thickness of the hcp layer(s) ranges from about 0.2 nm to 40 nm. More preferably, the thickness is about 1-20 nm.

The storage layer 17 may comprise one layer or any number of layers of magnetic material. Preferred materials for the storage layer 17 include Co with one or more elements selected from Pt, Cr, Ta, B, Cu, W, Mo, Ru, Ni, Nb, Zr, Hf. Optionally, one or more oxides of elements such as Si, Ti, Zr, Al, Cr, Co, Nb, Mg, Ta, W, or Zn may also be present in the storage layer 17. Preferably, the storage layer 17 is grown in a controlled atmosphere. Preferably, the controlled atmosphere includes Ar, Kr, or Xe or combination of these gasses with a reactive gas component such as O₂. The storage layer 17 may be grown at low temperatures, i.e. below 400 K. Typically, low temperatures are used for fabricating magnetic layers sputtered in controlled atmospheres including combinations of Ar, Kr, Xe and O₂. Alternatively, the storage layer 17 may be grown at elevated temperatures, i.e. above 400 K. Preferably, the elevated temperature is higher than 420 K and below 600 K.

In the present embodiment, the low-coupling magnetic layer 16 is located between non-magnetic interlayer 15 and the storage layer 17. In this embodiment, the crystallographic structure of the low-coupling magnetic layer 16 may be adjusted to improve the crystallographic growth of the storage layer 17. For example, for a storage layer(s) 17 with an hcp crystallographic structure, a low-coupling magnetic layer(s) 16 may be selected to have an hcp or fcc crystallographic structure, or it may be amorphous. Preferred materials for the low-coupling magnetic layer 16 include at least one of Fe, Co, Ni with one or more elements selected from Cr, Pt, Ta, B, Ru, Cu, Ag, Au, W, Mo, Nb, Zr, Hf, Ti, Zn, and Re. Preferably, the low-coupling magnetic layer 16 has a lower Ms than the Ms of the storage layer 17 to obtain weak direct exchange coupling. The storage layer 17 preferably has a Ms of approximately 400-900 emu/cm³. The low-coupling magnetic layer 16 preferably has a Ms less than or equal to about 600 emu/cm³. More preferably Ms is less than or equal to about 300 emu/cm³. Even more preferably, Ms is less than or equal to about 50 emu/cm³. Possible storage layer 17/low-coupling magnetic layer 16 combinations may be, but are not limited to: 600/300, 900/600, 500/50, 450/350, 600/450 and 900/400.

The topmost layer covering the low-coupling perpendicular magnetic recording media 10 of this embodiment is the carbon protective overcoat 18. The thickness of the carbon protective overcoat 18 may vary according to the desired life and durability of the low-coupling perpendicular magnetic recording media 10.

FIG. 2 illustrates a second preferred embodiment of the invention. The low-coupling perpendicular magnetic recording media 20 of this embodiment includes a substrate 11, an adhesion layer 12, a soft under layer 13, an amorphous layer 14, an non-magnetic interlayer 15, a storage layer 17, a low-coupling magnetic layer 16, and a carbon protective overcoat. That is, in contrast to the first embodiment, the low-coupling magnetic layer 16 is between the storage layer 17 and the carbon protective overcoat. Further, as in the first embodiment, the soft under layer 13, the amorphous layer 14, the non-magnetic interlayer 15, the storage layer 17, the low-coupling magnetic layer 16, and the carbon protective overcoat 18 may include multiple layers.

FIG. 3 illustrates a third preferred embodiment of the invention. The low-coupling perpendicular magnetic recording media 30 of this embodiment includes a substrate 11, an adhesion layer 12, a soft under layer 13, an amorphous layer 14, an non-magnetic interlayer 15, a first low-coupling magnetic layer 16 a, a storage layer 17, a second low-coupling magnetic layer 16 b, and a carbon protective overcoat. In contrast to the first embodiment, the low-coupling magnetic layer 16 comprises at least two layers that are separated by at least one storage layer 17. Further, the soft underlayer 13, the amorphous layer 14, the non-magnetic interlayer 15, the first low-coupling magnetic layer 16 a, the storage layer 17, the second low-coupling magnetic layer 16 b, and the carbon protective overcoat 18 may include multiple layers.

FIG. 4 illustrates a fourth preferred embodiment of the invention. The low-coupling perpendicular magnetic recording media 30 of this embodiment includes a substrate 11, an adhesion layer 12, a soft under layer 13, an amorphous layer 14, an non-magnetic interlayer 15, a low-coupling magnetic layer 16, a first storage layer 17 a, a second storage layer 17 b, and a carbon protective overcoat. In contrast to the first embodiment, the storage layer 17 comprises at least two layers that are separated by at least one low-coupling magnetic layer 16. Further, the soft underlayer 13, the amorphous layer 14, the non-magnetic interlayer 15, the first low-coupling magnetic layer 16, the first storage layer 17 a, the second storage layer 17 b, and the carbon protective overcoat 18 may include multiple layers.

FIG. 5 illustrates Monte Carlo simulations demonstrating improved recording properties of an embodiment of the invention having a thick low-coupling magnetic layer of hcp crystallographic structure with Ms=50 emu/cm³ located between a non-magnetic interlayer 15 and a storage layer 17. In particular, the Monte Carlo simulations illustrated in FIG. 5 show that optimal recording properties of perpendicular media can be achieved for media with very low and uniform direct exchange coupling (A*), wherein A* comprises a value of A*≈(0.05±0.03)*10⁻¹¹ J/m (FIG. 5). Such a low value of direct exchange coupling results from most sputtered Co-alloy thin films having low saturation magnetization in a range of about 50 emu/cc<Ms<300 emu/cc. Assumptions for the simulations include: a grain size dispersion of σ_(D)/D≈0.1, where σ_(D)/D describes a microstructure comprising a grain size defined by an average grain diameter (D) and a variation of grain size defined by a standard deviation (ED); anisotropy dispersion σ_(HA)/H_(A)≈0.02, where H_(A) is the average anisotropy field of grains comprising the media and σ_(HA) is the standard deviation of the anisotropy field; and linear density of 1270 kfci. Approximate values of σ_(D)/D and σ_(HA)/H_(A) can be experimentally obtained by microscopy techniques such as TEM and SEM, and magnetometry techniques such as Berger's method and AC transverse susceptibility respectively. Linear density is simply related to the length of each bit that is controlled by the recording process.

Similar model result trends to those shown for the specified model calculation parameters are obtained for a range of values of the model calculation parameters. Based on the results of the simulations, the inventors have determined that an additional low magnetization magnetic layer(s) 16 in perpendicular media structure provides lower exchange coupling between magnetic layers and grains in perpendicular media, which will significantly improve the performance. By varying Ms of the low magnetization magnetic layer 16, the strength of direct exchange coupling in perpendicular recording media can be controlled. Simulations demonstrate that the location of the low magnetization magnetic layer 16 can be between the non-magnetic interlayer 15 and the storage layer 17, or between the storage layer 17 and the carbon protective overcoat 18. Alternatively, the low magnetization magnetic layer 16 may be located between or adjacent to a plurality of storage layers 17, e.g., 17 a and 17 b shown in FIG. 4. Alternatively, the low magnetization magnetic layer 16 may comprise a plurality of low magnetization layers, such as layers 16 a, 16 b shown in FIG. 3, which can be located between the interlayer 15 and the storage layer 17 and between the storage layer 17 and the carbon protective overcoat 18. Preferably, Ms of low magnetization magnetic layer 16 is low, i.e. below about 600 emu/cm³ to provide low exchange coupling. More preferably, Ms is below about 300 emu/cm³. Even more preferably, Ms is below about 50 emu/cm³. The implementations described above and other implementations are within the scope of the following claims. 

1. A low-coupling perpendicular magnetic recording media comprising; a magnetic storage layer; and at least one low saturation magnetization layer, wherein the magnetic storage layer has a saturation magnetization between about 400-900 emu/cm³ and the at least one low saturation magnetization layer has a saturation magnetization below that of the magnetic storage layer.
 2. The low-coupling perpendicular magnetic recording media of claim 1 further comprising: a substrate; at least one soft underlayer; at least one non-magnetic interlayer; at least one storage layer; and a carbon protective overcoat.
 3. The low-coupling perpendicular magnetic recording media of claim 2, further comprising an adhesion layer selected from a group of materials including Cr, Ni, Ta, Ti, and alloys thereof.
 4. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one soft underlayer comprises at least one of Fe and Co with one or more elements selected from Ni, B, P, Si, C, Zr, Nb, Hf, Ta, Al, Si, Cu, Ag, Au.
 5. The low-coupling perpendicular magnetic recording media of claim 2, further comprising at least one amorphous layer, wherein the at least one amorphous layer comprises elements and alloys comprising Ta, Ti, Ni, Cr, Zr, Nb, and P, or an amorphous ferromagnetic material comprising Fe with one or more of the elements selected from the group consisting of Co, B, P, Si, C, Zr, Nb, Hf, Ta, Al, Cu, Ag, and Au.
 6. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one non-magnetic interlayer comprises an fcc layer selected from the group consisting of Cu, Ag, Au, Ir, Ni, Pt, Pd and alloys thereof.
 7. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one non-magnetic interlayer comprises an hcp layer selected from the group consisting of Co, Ru, Re, Hf, Ti, Zr and alloys thereof or CoCr with one or more of the elements selected from the group consisting Ta, B, Pt, Nb, Ru, and Zr.
 8. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one storage layer comprises a magnetic layer selected from the group consisting of Co with one or more elements selected from the group consisting of Pt, Cr, Ta, B, Cu, W, Mo, Ru, Ni, Nb, Zr, Hf.
 9. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one storage layer comprises one or more oxides selected from group consisting of oxides of Si, Ti, Zr, Al, Cr, Co, Nb, Mg and Zn.
 10. The low-coupling perpendicular magnetic recording media of claim 2, wherein the at least one low saturation magnetization magnetic layer comprises at least one of Fe, Co, or Ni with one or more elements selected from the group consisting of Cr, Pt, Ta, B, Ru, Cu, Ag, Au, W, Mo, Nb, Zr, Hf, Ti, Zn, and Re.
 11. The low-coupling perpendicular magnetic recording media of claim 2, wherein the low saturation magnetization magnetic layer is located between the at least one non-magnetic interlayer and the at least one storage layer.
 12. The low-coupling perpendicular magnetic recording media of claim 2, wherein the low saturation magnetization magnetic layer is located between the at least storage layer and the carbon protective overcoat.
 13. The low-coupling perpendicular magnetic recording media of claim 2, comprising a first storage layer located between the at least one non-magnetic interlayer and the at least one low saturation magnetization magnetic layer, and a second storage layer located between the at least low saturation magnetization magnetic layer and the carbon protective overcoat.
 14. The low-coupling perpendicular magnetic recording media of claim 2, comprising a first low saturation magnetization magnetic layer located between the at least one non-magnetic interlayer and the at least one storage layer and a second low saturation magnetization magnetic layer located between the at least storage layer and the carbon protective overcoat.
 15. The low-coupling perpendicular magnetic recording media of claim 2, wherein the low saturation magnetization magnetic layer has a magnetization below 300 emu/cm³.
 16. The low-coupling perpendicular magnetic recording media of claim 2, wherein the low saturation magnetization magnetic layer has a magnetization below 50 emu/cm³.
 17. A method of making a low-coupling perpendicular magnetic recording media comprising: depositing a soft underlayer; depositing an non-magnetic interlayer; depositing a magnetic storage layer; and depositing a low saturation magnetization magnetic layer, wherein the magnetic storage layer has a saturation magnetization between about 400-900 emu/cm³ and the low saturation magnetization layer has a saturation magnetization below that of the magnetic storage layer.
 18. The method of claim 17, further comprising depositing an amorphous layer on the soft underlayer.
 19. The method of claim 17, further comprising depositing a second low saturation magnetization magnetic layer.
 20. A method comprising: obtaining a storage media having a magnetic storage layer with a saturation magnetization between about 400-900 emu/cm³ and at least one low saturation magnetization layer with a saturation magnetization below that of the magnetic storage layer.
 21. The method of claim 19, wherein the magnetic storage layer has a saturation magnetization equal to or above 600 emu/cm³ and the at least one low saturation magnetization layer has a saturation magnetization equal to or below 300 emu/cm³. 